Safe and 201 is a kind of stainless steel. 201 stainless steel generally refers to 201 stainless steel and acid resistant steel. 201 stainless steel refers to the steel that is resistant to the corrosion of weak media such as atmosphere, steam and water, while acid resistant steel refers to the steel that is resistant to the corrosion of chemical corrosive media such as acid, alkali and salt.This product is a high manganese and low nickel stainless steel with low nickel content and poor corrosion resistance. It is widely used in various tabletops, countertops, kitchenware, outdoor decoration engineering, urban decoration industry and low-grade household products.
201 Stainless Steel Flat Bar Specification
| Product | 201 Stainless Steel Flat Bar | Grade | 200 series：201, 202 etc. |
| Thickness | 0.2-300mm or as required | 300 series：304, 304L, 316, 316L, 301, 302, 303, 309, 309S, 310, 310S, 321, 904L etc. | |
| Width | 0.12-2.0mm or as required | 400 series：410, 420, 430, 440 etc. | |
| Length | 1-12m or as required | Duplex stainless：2205, 2507 2304 etc. | |
| Standard | ASTM,JIS,SUS,GB,DIN | Other：1.4410, 1.4362, 254SOM etc. | |
| Technique | Hot rolled / Cold rolled | Surface | 2B,BA,No.1,No.4,No.8,8K,Mirror,Checkered,Embossed,Hairline,Sand Blast,StainBrush,Etching,etc. |
201 Stainless Steel Chemical Composition
| Element | Content (%) |
| Iron, Fe | 72 |
| Chromium, Cr | 16.0 – 18.0 |
| Manganese, Mn | 5.50 – 7.50 |
| Nickel, Ni | 3.50 – 5.50 |
| Silicon, Si | 1.0 |
| Nitrogen, N | 0.25 |
| Carbon, C | 0.15 |
201 Stainless Steel Mechanical Properties
| Properties | Metric | Imperial |
| Tensile strength (transverse at room temperature) | 685 MPa | 99400 psi |
| Tensile strength (longitudinal at room temperature) | 696 MPa | 101000 psi |
| Yield strength (transverse at room temperature) | 292 MPa | 42400 psi |
| Yield strength (longitudinal at room temperature) | 301 MPa | 43700 psi |
| Compressive strength | 365 MPa | 52900 psi |
| Elastic modulus | 197 GPa | 28573 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (longitudinal at room temperature) | 56% | 56% |
| Elongation at break (transverse at room temperature) | 62.50% | 62.50% |
| Hardness, Rockwell B (transverse at room temperature) | 85 | 85 |
| Hardness, Rockwell B (longitudinal at room temperature) | 85 | 85 |
| stainless steel flat bar lowes | hot sale stainless steel flat bar |
| stainless steel flat bar prices | stainless steel flat bar suppliers |
| stainless steel flat bar suppliers | steel angle flat bar list |
| stainless steel flat bar with holes | high quality stainless steel flat bar |
| stainless steel flat bar suppliers | stainless steel flat bar manufacturer |
| stainless steel flat bar price | China stainless steel flat bar |
| stainless steel flat bar profile | stainless steel t flat bar from China |
| stainless steel flat bar rings | stainless steel flat bar |
Payment methods we support
Quote Online
Contact Us