1.Wide flange, high lateral stiffness.
2.H-beam has good bending resistance, about 5%-10% better than i-bar.
3.The two surfaces of flange are parallel to each other, which makes connection, processing and installation easy.
4.Compared with welding i-steel, H beam is low cost, high precision, small residual stress, no need for expensive welding materials and weld inspection, saving about 30% of the production cost of steel structure.
5.Under the same section load, the weight of hot-rolled H beam steel structure can be reduced by 15%-20% compared with traditional steel structure.
6.Compared with concrete structure, hot-rolled H beam steel structure can increase the usable area by 6%, reduce the dead weight by 20%-30%, and reduce the internal force of structure design.
7.H-beam can be processed into T beam, honeycomb beam can be combined to form a variety of sections, greatly meet the needs of engineering design and production. 

430 Stainless Steel H-Beams Specification

430 Stainless Steel H-Beams Chemical Composition

430 Stainless Steel H-Beams Mechanical Properties

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
430	483	310	22	85	183