304 stainless steel is the most widely used chromium nickel stainless steel. As a widely used steel, it has good corrosion resistance, heat resistance, low temperature strength and mechanical properties; Good hot workability such as stamping and bending, no heat treatment hardening phenomenon (service temperature -196 ℃ ~ 800 ℃). It is corrosion-resistant in the atmosphere. If it is an industrial atmosphere or a heavily polluted area, it needs to be cleaned in time to avoid corrosion. Suitable for food processing, storage and transportation. It has good machinability and weldability.
304L stainless steel plate is better than 304 in pitting corrosion resistance at welding points or other treatment places. 304L is more corrosion resistant, with excellent corrosion resistance, heat resistance, low temperature strength and mechanical properties; Good hot workability such as stamping meandering, no heat treatment hardening scene (no magnetism, application temperature - 196 ° C ~ 800 ° C), and excellent grain boundary corrosion resistance after 304L welding or stress elimination; It can also adhere to excellent corrosion resistance without heat treatment, and the application temperature is - 196 ° c-800 ° C.

304/304L Stainless Steel Angle Specification

Chemical Composition

Mechanical Properties

Property	304	304L
Yield Strength, min. (ksi)	30	25
Tensile Strength, min. (ksi)	75	70
Elongation, min. (%)	40	40
Hardness, max. (Rb)	92	92